Stainless steel 904l round pipes sizes

<ul><li>1/8" (3.175 mm) to 12" (304.8 mm)</li><li>Sch 5 to Sch 160</li><li>As per ASTM A269, ASTM A312, ASTM A358</li><li>NPS (Nominal Pipe Size) and DN (Diameter Nominal) are used interchangeably and they refer to the same pipe size</li></ul>

Stainless steel 904l round pipes pressure rating

The pressure rating of a stainless steel 904L round pipe depends on several factors, including the pipe's size, wall thickness, and the material's yield strength.Pressure rating for 904L round pipe can be calculated using the following formula:P = (2 * S * t) / (D o - t)

Stainless steel 904l round pipes mechanical properties

<ul><li>Yield Strength: 220 MPa (min) - 310 MPa (max)</li><li>Tensile Strength: 480 MPa (min) - 620 MPa (max)</li><li>Elongation: 35% (min)</li><li>Hardness: 220-280 Vickers (typical)</li><li>Impact Toughness: Not specified</li><li>Density: 7.95 g/cm3</li></ul>

Equivalent of stainless steel 904l round pipes

<ul><li>UNS N08904</li><li>SAE J405: 904L / UNS N08904</li><li>DIN 1.4539</li><li>EN 1.4539 / X1NiCrMoCu25-20-5</li><li>ASTM A269 / A312 / A358 / A778</li><li>JIS G3459 / G3463</li><li>GB/T 12771 / 13296</li><li>ISO 9329-5 / ISO 9330-5</li><li>GOST 03Ch17N14M3</li></ul>

Top-Rated 904L Stainless Steel Round Pipe Suppliers

1/8" (3.175 mm) to 12" (304.8 mm)
Sch 5 to Sch 160
As per ASTM A269, ASTM A312, ASTM A358
NPS (Nominal Pipe Size) and DN (Diameter Nominal) are used interchangeably and they refer to the same pipe size

The pressure rating of a stainless steel 904L round pipe depends on several factors, including the pipe's size, wall thickness, and the material's yield strength.

Pressure rating for 904L round pipe can be calculated using the following formula:

P = (2 * S * t) / (D o - t)

Yield Strength: 220 MPa (min) - 310 MPa (max)
Tensile Strength: 480 MPa (min) - 620 MPa (max)
Elongation: 35% (min)
Hardness: 220-280 Vickers (typical)
Impact Toughness: Not specified
Density: 7.95 g/cm3

Price is based on the various factors, in general, it starts from INR 450/Kg to INR 700/Kg

UNS N08904
SAE J405: 904L / UNS N08904
DIN 1.4539
EN 1.4539 / X1NiCrMoCu25-20-5
ASTM A269 / A312 / A358 / A778
JIS G3459 / G3463
GB/T 12771 / 13296
ISO 9329-5 / ISO 9330-5
GOST 03Ch17N14M3

The density of 904L stainless steel pipes is approximately 8.0 g/cm3 (grams per cubic centimeter). This material is a low-carbon, high-nickel, molybdenum austenitic stainless steel alloy with good weldability and formability properties. It has higher resistance to pitting and crevice corrosion compared to other grades of stainless steel due to its high levels of chromium, nickel and molybdenum. Its corrosion resistance makes it suitable for use in applications involving sulfuric acid at temperatures below 85 degrees Celsius. It is also used in the manufacture of pharmaceutical equipment such as storage tanks, pipes, pumps and valves.

The hardness of 904L stainless steel pipes is around 230 HB (Brinell), which is relatively soft compared to other grades of stainless steel. It has excellent formability and weldability properties, allowing for easy fabrication and installation. It also exhibits good strength and fatigue resistance at elevated service temperatures. This material can be hardened by cold-working processes such as cold rolling, spinning or pressing, and it is often used in applications involving pressure vessels and valves. Its corrosion resistance makes it a popular choice for chemical processing, oil refining, paper production and food processing industries.