Stainless Steel 201 Screw

Stainless Steel 201 screws are fasteners that are manufactured from a chromium-nickel-manganese alloy that is characterized by good corrosion resistance, optimal strength, and relatively high durability. They are relatively cheaper but with good performance and can be used both indoors and outdoors.

Chemical compositions of Stainless Steel 201 Screw

Stainless Steel 201 screws are made from commercially pure titanium with the following typical chemical composition:

Element	Content (%)
Iron, Fe	72
Chromium, Cr	16.0 - 18.0
Manganese, Mn	5.50 - 7.50
Nickel, Ni	3.50 - 5.50
Silicon, Si	1.0
Nitrogen, N	0.25
Carbon, C	0.15

This information is useful in evaluating the stainless Steel 201 screws' performance under different operating conditions.

Mechanical properties of Stainless Steel 201 Screw

Stainless Steel 201 screws possess several key mechanical properties:

Properties	Metric	Imperial
Tensile strength (transverse at room temperature)	685 MPa	99400 psi
Tensile strength (longitudinal at room temperature)	696 MPa	101000 psi
Yield strength (transverse at room temperature)	292 MPa	42400 psi
Yield strength (longitudinal at room temperature)	301 MPa	43700 psi
Compressive yield strength	365 MPa	52900 psi
Elastic modulus	197 GPa	28573 ksi
Poisson's ratio	0.27-0.30	0.27-0.30
Elongation at break (longitudinal at room temperature)	56%	56%
Elongation at break (transverse at room temperature)	62.50%	62.50%
Hardness, Rockwell B (transverse at room temperature)	85	85
Hardness, Rockwell B (longitudinal at room temperature)	85	85

These properties ensure that Stainless Steel 201 screws offer an all-round performance making them suitable for various industrial applications.

Features of Stainless Steel 201 Screw

Stainless Steel 201 screws offer several notable features due to their unique composition and properties which include:

Cost-Effective: Stainless Steel 201 screws are usually cheaper compared to other grades of stainless steel such as the 304 and 316 grades.
Strength: Stainless Steel 201 screws provide Good tensile and shear strength to be used for different fastening purposes.
Aesthetic Finish: Stainless Steel 201 screws usually provide a shiny and attractive finish that does not easily tarnish.
Non-Magnetic: Although Stainless Steel 201 screws are not a fully non-magnetic material, their magnetic performance is comparatively lower than other stainless-based metals.
Formability: Stainless Steel 201 screws can be easily machined and shaped to enable its use in many different ways.
Durability: Stainless Steel 201 screws offer enhanced durability and stability in different conditions and settings.
Resistance to Staining: Stainless Steel 201 screws are Good for preventing staining when the fabric comes into contact with different chemicals.
Temperature Tolerance: Stainless Steel 201 screws can work at a variety of temperatures, but is not as heat-tolerant as other grades of the alloy.
Ease of Installation: Stainless Steel 201 screws comes with an easily driven design and a fastening mechanism that is easy to operate.
Low Maintenance: Stainless Steel 201 screws do not require much maintenance because they are not easily affected by oxidation or tarnishing.

These features contribute to the versatility and reliability of Stainless Steel 201 screws in various demanding applications.

Uses of Stainless Steel 201 Screw

Stainless Steel 201 screws are utilized in a range of industries due to their unique properties. These bars are commonly used in industrial settings.

Construction: Stainless Steel 201 screws are applied where the building structures, fixtures, and fittings that require a moderate degree of corrosion protection.
Automotive Industry: Stainless Steel 201 screws are used in auto manufacturing industries, especially in areas that do not require heavy gauges for strength but need rust protection in vehicle assembling and repair.
Household Items: Stainless Steel 201 screws are used in appliances furniture and home fixtures because they offer durability and give the appearance of elegance.
Electronics: Stainless Steel 201 screws are equipped in applications such as electronic devices and housing where corrosion is a concern but the cost is a limiting factor.
Manufacturing: Stainless Steel 201 screws are applied in machinery and equipment construction, where moderate strength and resistance to oxidation are needed.
Interior Applications: Stainless Steel 201 screws are best for interiors where conditions such as humidity are not going to come into play.
Retail Fixtures: Stainless Steel 201 screws are used in displays, racks, and shelving units because of their smooth look and ability to withstand wear.
HVAC Systems: Stainless Steel 201 screws are also applied in heating, ventilation, and air conditioning systems when moderate corrosion resistance is required.
Industrial Equipment: Stainless Steel 201 screws are used in numerous construction of industrial tools and instrument parts.
Marine Applications: Stainless Steel 201 screws are best used where there is little or no exposure to salt water since the sealant will degrade under these conditions.
Agricultural Equipment: Stainless Steel 201 screws are also applied in tractors and other farming implements where it can be advantageous to have additional protection against rusting.

Thus, Stainless Steel 201 screws can withstand extreme conditions, making them a preferred choice for critical applications.

Chemical compositions of Stainless Steel 201 Screw

Stainless Steel 201 screws are made from commercially pure titanium with the following typical chemical composition:

Element	Content (%)
Iron, Fe	72
Chromium, Cr	16.0 - 18.0
Manganese, Mn	5.50 - 7.50
Nickel, Ni	3.50 - 5.50
Silicon, Si	1.0
Nitrogen, N	0.25
Carbon, C	0.15

This information is useful in evaluating the stainless Steel 201 screws' performance under different operating conditions.

Mechanical properties of Stainless Steel 201 Screw

Stainless Steel 201 screws possess several key mechanical properties:

Properties	Metric	Imperial
Tensile strength (transverse at room temperature)	685 MPa	99400 psi
Tensile strength (longitudinal at room temperature)	696 MPa	101000 psi
Yield strength (transverse at room temperature)	292 MPa	42400 psi
Yield strength (longitudinal at room temperature)	301 MPa	43700 psi
Compressive yield strength	365 MPa	52900 psi
Elastic modulus	197 GPa	28573 ksi
Poisson's ratio	0.27-0.30	0.27-0.30
Elongation at break (longitudinal at room temperature)	56%	56%
Elongation at break (transverse at room temperature)	62.50%	62.50%
Hardness, Rockwell B (transverse at room temperature)	85	85
Hardness, Rockwell B (longitudinal at room temperature)	85	85

These properties ensure that Stainless Steel 201 screws offer an all-round performance making them suitable for various industrial applications.

Features of Stainless Steel 201 Screw

Stainless Steel 201 screws offer several notable features due to their unique composition and properties which include:

Cost-Effective: Stainless Steel 201 screws are usually cheaper compared to other grades of stainless steel such as the 304 and 316 grades.
Strength: Stainless Steel 201 screws provide Good tensile and shear strength to be used for different fastening purposes.
Aesthetic Finish: Stainless Steel 201 screws usually provide a shiny and attractive finish that does not easily tarnish.
Non-Magnetic: Although Stainless Steel 201 screws are not a fully non-magnetic material, their magnetic performance is comparatively lower than other stainless-based metals.
Formability: Stainless Steel 201 screws can be easily machined and shaped to enable its use in many different ways.
Durability: Stainless Steel 201 screws offer enhanced durability and stability in different conditions and settings.
Resistance to Staining: Stainless Steel 201 screws are Good for preventing staining when the fabric comes into contact with different chemicals.
Temperature Tolerance: Stainless Steel 201 screws can work at a variety of temperatures, but is not as heat-tolerant as other grades of the alloy.
Ease of Installation: Stainless Steel 201 screws comes with an easily driven design and a fastening mechanism that is easy to operate.
Low Maintenance: Stainless Steel 201 screws do not require much maintenance because they are not easily affected by oxidation or tarnishing.

These features contribute to the versatility and reliability of Stainless Steel 201 screws in various demanding applications.

Uses of Stainless Steel 201 Screw

Stainless Steel 201 screws are utilized in a range of industries due to their unique properties. These bars are commonly used in industrial settings.

Construction: Stainless Steel 201 screws are applied where the building structures, fixtures, and fittings that require a moderate degree of corrosion protection.
Automotive Industry: Stainless Steel 201 screws are used in auto manufacturing industries, especially in areas that do not require heavy gauges for strength but need rust protection in vehicle assembling and repair.
Household Items: Stainless Steel 201 screws are used in appliances furniture and home fixtures because they offer durability and give the appearance of elegance.
Electronics: Stainless Steel 201 screws are equipped in applications such as electronic devices and housing where corrosion is a concern but the cost is a limiting factor.
Manufacturing: Stainless Steel 201 screws are applied in machinery and equipment construction, where moderate strength and resistance to oxidation are needed.
Interior Applications: Stainless Steel 201 screws are best for interiors where conditions such as humidity are not going to come into play.
Retail Fixtures: Stainless Steel 201 screws are used in displays, racks, and shelving units because of their smooth look and ability to withstand wear.
HVAC Systems: Stainless Steel 201 screws are also applied in heating, ventilation, and air conditioning systems when moderate corrosion resistance is required.
Industrial Equipment: Stainless Steel 201 screws are used in numerous construction of industrial tools and instrument parts.
Marine Applications: Stainless Steel 201 screws are best used where there is little or no exposure to salt water since the sealant will degrade under these conditions.
Agricultural Equipment: Stainless Steel 201 screws are also applied in tractors and other farming implements where it can be advantageous to have additional protection against rusting.

Thus, Stainless Steel 201 screws can withstand extreme conditions, making them a preferred choice for critical applications.

bright metal overseas llp

mumbai - maharashtra - india

1 Year

View Profile

bright metal overseas llp

mumbai - maharashtra - india

1 Year

View Profile

Stainless Steel 201 Screw FAQ's

Stainless Steel 201 Screw Starts At Rs 10/Piece To Rs 15/Piece.

Yes, Stainless Steel 201 Screws offer excellent corrosion resistance against most acids and alkalis in a variety of temperatures and concentrations. This makes them well-suited for use in industries such as food processing and marine engineering where corrosive liquids are commonly used.

Yes, Stainless Steel 201 Screws are susceptible to rust if exposed to wet or highly corrosive environments. To prevent this, they must be treated or coated with a protective layer such as paint or powder coating.

No more suppliers available.